Abstract
In this study, we report the production of β˝-Al2O3 solid electrolyte by using Seydişehir α-Al2O3. Alumina has to be low grain-sized to ensure α-β phase transformation. Therefore, grain refining process was applied to high grain sized Seydişehir alumina by jetmill grinding. Seydişehir alumina was calcined at 1200 0C for 2 hours. After calcination, calcined Al2O3 and Na2CO3 were mixed during 2 hours in the mill. The samples were pressed and sintered to obtain β˝-Al2O3. β˝-Al2O3 was obtained after sintering at 1550°C for 1 hour. Due to the formation of β˝-Al2O3, it is observed that dielectric properties increased.
Keywords
Electrolyte
Chemistry
Production (economics)
Analytical Chemistry (journal)
Materials science
Physical chemistry
Environmental chemistry
Electrode
Subject Areas
Advanced ceramic materials synthesis
·Ceramics and Composites ·Physical Sciences
Microwave Dielectric Ceramics Synthesis
·Electrical and Electronic Engineering ·Physical Sciences
Concrete and Cement Materials Research
·Civil and Structural Engineering ·Physical Sciences
Citations by Year
2019: 1
2020: 1
Loading…
Loading…